Viscosity @ 30°C
660 cP
Shore D
89-90
Izod Notched Impact
20 J/m
Heat Deflection Temperature
58°C @ 1.82 MPa
Vickers Hardness
18 HV
Young's Modulus, Dry Material
1340 MPa
Young's Modulus, After Immersion in Water 2 Days -37°C
1330 MPa
Ultimate Strength, Dry Material
67.5 MPa
Ultimate Strength, After Immersion in Water 2 Days -37°C
68.9 MPa
Strain at Break, Dry Material
16%
Strain at Break, After Immersion in Water 2 Days -37°C
14%
Ultimate Flexural Strength, Dry Material
136 MPa
Ultimate Flexural Strength, After Immersion in Water 2 Days -37°C
120 MPa
Flexural Modulus, Dry Material
3660 MPa
Flexural Modulus, After Immersion in Water 2 Days -37°C